Vacuum forming is a manufacturing method used to shape a heated sheet of plastic around a certain mold using the force of a vacuum. It's great advantage is fast production of parts with minimal post processing. There are different methods to vacuum forming. The mold, also called the tool, can be either male or female. Male tools are used if precision is needed on the inside of the part. Female tools, often used with plugs, are used for precision on the outside of the part. Most industrial molds are machined from metal blocks, such aluminum. Although, the use of machined molds can get expensive as they are hard to make and can have a long lead time. If the tool needs replacing or modification, it can create a lot of down time. This is where 3D printed molds come in handy. They are not as durable as machined molds, but are ideal for fast prototyping. The complication with 3D printed molds is that filament is also a thermoplastic, which melts under heat. So how do you keep the integrity of your mold when in comes into contact with a very hot plastic sheet? This is what we will be covering in this document as to how to prepare your molds to perform as best as possible in the vacuum forming process.
 
Vacuum forming is a manufacturing method used to shape a heated sheet of plastic around a certain mold using the force of a vacuum. It's great advantage is fast production of parts with minimal post processing. There are different methods to vacuum forming. The mold, also called the tool, can be either male or female. Male tools are used if precision is needed on the inside of the part. Female tools, often used with plugs, are used for precision on the outside of the part. Most industrial molds are machined from metal blocks, such aluminum. Although, the use of machined molds can get expensive as they are hard to make and can have a long lead time. If the tool needs replacing or modification, it can create a lot of down time. This is where 3D printed molds come in handy. They are not as durable as machined molds, but are ideal for fast prototyping. The complication with 3D printed molds is that filament is also a thermoplastic, which melts under heat. So how do you keep the integrity of your mold when in comes into contact with a very hot plastic sheet? This is what we will be covering in this document as to how to prepare your molds to perform as best as possible in the vacuum forming process.
  
Line 11: Line 11:
 
=== Undercuts ===
 
=== Undercuts ===
 
Similarly to the reason we apply draft angles, we avoid undercuts to prevent the risk of our mold getting stuck. A good way to avoid them is to ask yourself if your 3D part needs supports. If it does, then chances are that your mold will get stuck in your vacuum formed part.
 
Similarly to the reason we apply draft angles, we avoid undercuts to prevent the risk of our mold getting stuck. A good way to avoid them is to ask yourself if your 3D part needs supports. If it does, then chances are that your mold will get stuck in your vacuum formed part.
[[File:Undercuts.png|center|thumb|577x577px|Comparison between annon-removable undercut (left) and a removable undercut (right)]]
+
[[File:Undercuts.png|center|thumb|577x577px|Comparison between a non-removable undercut (left) and a removable undercut (right)]]
  
 
=== Possible Depths ===
 
=== Possible Depths ===
Line 62: Line 62:
 
It is important to keep in mind that melting a plastic emits toxic fumes. Although a vacuum form machine doesn't completely melt plastics, it does bring it past it's glass transition temperature, where polymer chains are allowed to move some encounter thermal decomposition. "During thermal decomposition, polymers breakdown into hazardous plastic fumes, fatty acids, and the original manufacturing compounds."<ref>[https://www.sentryair.com/plastic-fumes.htm#:~:text=During%20thermal%20decomposition%2C%20polymers%20breakdown,fires%20in%20a%20burning%20building. Plastic Fumes - Sentry Air Systems]</ref>  Material choice is important not only for your project, but also the safety of the people working int the same space. Have your material approved by staff before using it. '''Do not leave heaters unattended and do not overheat plastic sheets!''' Doing so will increase the risk of releasing toxic fume.
 
It is important to keep in mind that melting a plastic emits toxic fumes. Although a vacuum form machine doesn't completely melt plastics, it does bring it past it's glass transition temperature, where polymer chains are allowed to move some encounter thermal decomposition. "During thermal decomposition, polymers breakdown into hazardous plastic fumes, fatty acids, and the original manufacturing compounds."<ref>[https://www.sentryair.com/plastic-fumes.htm#:~:text=During%20thermal%20decomposition%2C%20polymers%20breakdown,fires%20in%20a%20burning%20building. Plastic Fumes - Sentry Air Systems]</ref>  Material choice is important not only for your project, but also the safety of the people working int the same space. Have your material approved by staff before using it. '''Do not leave heaters unattended and do not overheat plastic sheets!''' Doing so will increase the risk of releasing toxic fume.
  
=== Trapping ===
+
=== Pinching ===
There is a risk of trapping when operating the vacuum form machine. Use caution when using the clamp frame to ensure fingers or hands will not get trapped. This is a single person operating machine. Use caution when someone else is around.​
+
There is a risk of pinching when operating the vacuum form machine. Use caution when using the clamp frame to ensure fingers or hands will not get trapped. This is a single person operating machine. Use caution when someone else is around. The heaters also operate on rollers and track. You should not be putting your hands onto the track as it creates another risk of pinching.​
  
 
 
  
 
== References ==
 
== References ==

Latest revision as of 17:55, 29 August 2024

Formech 450DT

Vacuum forming is a manufacturing method used to shape a heated sheet of plastic around a certain mold using the force of a vacuum. It's great advantage is fast production of parts with minimal post processing. There are different methods to vacuum forming. The mold, also called the tool, can be either male or female. Male tools are used if precision is needed on the inside of the part. Female tools, often used with plugs, are used for precision on the outside of the part. Most industrial molds are machined from metal blocks, such aluminum. Although, the use of machined molds can get expensive as they are hard to make and can have a long lead time. If the tool needs replacing or modification, it can create a lot of down time. This is where 3D printed molds come in handy. They are not as durable as machined molds, but are ideal for fast prototyping. The complication with 3D printed molds is that filament is also a thermoplastic, which melts under heat. So how do you keep the integrity of your mold when in comes into contact with a very hot plastic sheet? This is what we will be covering in this document as to how to prepare your molds to perform as best as possible in the vacuum forming process.

3D Modeling your Mold

To succeed at vacuum forming it starts way before using the machine. A good mold is the foundation of a good part, with as little complications along the way.

Draft Angles

When vacuum forming your part, you want to avoid your mold getting stuck into it. To avoid this issue, we implement draft angles to all sides of the 3D model to ease the release of the mold. The recommended angle is 5° to 7° for male molds and 2° to 3° for female molds.

Note the difference between draft angles and the importance of choosing the right orientation

Undercuts

Similarly to the reason we apply draft angles, we avoid undercuts to prevent the risk of our mold getting stuck. A good way to avoid them is to ask yourself if your 3D part needs supports. If it does, then chances are that your mold will get stuck in your vacuum formed part.

Comparison between a non-removable undercut (left) and a removable undercut (right)

Possible Depths

A plastic sheet only has a certain amount of material available to form a mold. There is a limit to the amount a material is capable to draw. There are formulas and guidelines available to determine that limit. When it comes to cavities, the maximum depth should not exceed 75% of the opening.

Demonstration of reachable depths

Draw Ratio

Similarly as cavities, there is a maximum height you can have with your mold for a given sheet thickness. If you want your wall thickness of your final part to be a certain thickness, then you will use the draw ratio to find out which sheet thickness is best suited for your project. Here are the steps to calculate the draw ratio:

- Step 1: Calculate the surface area.

Using a CAD modeling software, you can easily get the surface area of your mold. If you do not have the exact number, you can approximate it by taking general measurements and assuming it as a simple geometry.


-Step 2: Calculate the footprint.

The footprint is the heated area of the plastic sheet and can be easily found if you know the dimensions of your machine.


-Step 3: Calculate the draw ratio.

To find the draw ratio, divide the surface area by the footprint.


Whichever number you end up with, you can multiply it by the desired wall thickness to find the starting gauge of your plastic sheet.

Edges / Fillets

Whenever you create a part for vacuum forming, you want to avoid sharp edges or sharp angles as much as possible. The thicker your plastic is, the less capable it will be to take the shape of those sharp corners. The thinner the material is, the more susceptible it is to overstretching.

Example of smoothing out corners for easier part forming

Air Holes

For the plastic sheet to be able to take the shape of your mold, air needs to be able to escape from between them. To help achieve so, we implement air holes at strategically placed locations. In general, these locations imply any area that is lower than it's surrounding such as cavities, where an air pocket can easily be formed. Air holes should be spaced at least 25mm apart and their diameter should be around 1mm for sheets up to 2mm in thickness and 1.5mm diameter for materials above 2mm in thickness. Materials under 1mm in thickness may require 0.75mm holes, such as polypropylene that will tend to seek out any holes or gaps in tooling.


It is ok to add air holes directly in your 3D model but it will increase print time unnecessarily. It is recommended instead to drill the holes manually with the correct drill bit size and protective gear. You can visit the VAQUFORM page where they talk more in depth about air holes.

Printer Settings

Once your 3D model of your mold is complete, it is time to print it. This is the part where slicer settings and filament selection will help the most towards the durability of your mold. Visit the VAQUFORM page for a detailed explanation on how to make your prints.

Health and Safety with Vacuum Forming

Vacuum forming is a generally safe machine that takes little effort to manufacture parts with great quality. Although, there still are safety aspects to take into consideration. When you encounter a problem with the machine, it is important to alert the staff about it and DO NOT attempt to fix it yourself. Reparations and changes to the machine should only be made by qualified personnel.

Burns

Evidently, the vacuum form machine uses heat reaching up to 300°C to soften the plastic. Consequently, some parts of the machine can get very very hot. It is important to know which those are and keep body parts clear of these area. The plastic part will also be very hot after forming. You should let it cool down before attempting to handle it. If you must handle the part immediately after forming, wear the proper PPE such as heat protective gloves. To test to see if the part is still hot, approach it gently with the back of your hand. If you can feel the heat without touching it, it is probably too hot to handle. If you cannot feel any heat from a distance, try and get closer until you can touch it rapidly without feeling excessive heat. From there it should be safe to touch the part without getting burned instantly and gauge if you can handle it or not.

Toxic Fumes

It is important to keep in mind that melting a plastic emits toxic fumes. Although a vacuum form machine doesn't completely melt plastics, it does bring it past it's glass transition temperature, where polymer chains are allowed to move some encounter thermal decomposition. "During thermal decomposition, polymers breakdown into hazardous plastic fumes, fatty acids, and the original manufacturing compounds."[1] Material choice is important not only for your project, but also the safety of the people working int the same space. Have your material approved by staff before using it. Do not leave heaters unattended and do not overheat plastic sheets! Doing so will increase the risk of releasing toxic fume.

Pinching

There is a risk of pinching when operating the vacuum form machine. Use caution when using the clamp frame to ensure fingers or hands will not get trapped. This is a single person operating machine. Use caution when someone else is around. The heaters also operate on rollers and track. You should not be putting your hands onto the track as it creates another risk of pinching.​